TCR characteristics of wear-resistant material specification table
TCR shot high wear-resistant material elastic properties spec sheet
Recipe Name |
EVA-140-60 | TCR-130-60 | Method&Conditions Test methods and conditions |
International standard | Standard | ||
Tensele strength tensile strength | 18↑ | 20↑ | ASTMD412 Temp:23±2℃ Speed:500mm/min |
Elongation Elongation | 250↑ | 380↑ | ASTMD412 Temp:23±2℃ Speed:500mm/min |
Tear strength Tear strength | 8↑ | 12↑ | ASTMD624 Temp:23±2℃ Speed:500mm/min |
Split tear Layered Tear | 2↑ | 3.5↑ | ks-08 Temp:23±2℃ Speed:200mm/min |
Hardness Hardness | 55~60(Skin - side) 50~55(Peel - Side) | 55~60(Skin - side) 50~55(Peel - Side) | ASTMD2240 Temp:23±2℃ Load:1kg |
Specific Gravity Density | 0.22~0.3 | 0.38~0.45 | ks-06-01 Temp:23±2℃ |
Shrinkage Shrink | 2↓ | 2↓ | ks-07 Temp:23±2℃ Time:40min |
Compression set Compression distortion | 65↓ | 45↓ | ASTMK395,METHODB Temp:50±2℃ Time:6Hours |
Din Abrasion Wear | 200↓ | 150↓ | DIN53516 Temp:23±2℃ Load:10kg |
Slip Slip | 0.6↑ | 0.8↑ | ks-09 load:6LB*3300 Cycle,Angle 15° |
Remark | |||
Audit: Wang Choi | Making: Laboratory |